型號
|
化學成份（%）
|
|
Si
|
Mg
|
Re
|
Ca
|
Ni
|
Ba
|
Bi
|
Sb
|
Al
|
|
一、普通球化劑
|
|
|
|
|
|
|
|
|
|
|
HTQ-5
|
40-45
|
5-6
|
1.0-1.5
|
1.5-2.5
|
|
|
|
|
<1.0
|
|
HTQ-5A
|
40-45
|
5-6
|
1.5-2.0
|
2.0-3.0
|
|
|
|
|
<1.0
|
|
HTQ-6
|
40-45
|
5.8-6.3
|
0.8-1.3
|
2.5-3.0
|
|
1.0-2.0
|
|
|
<1.0
|
|
HTQ-6A
|
40-45
|
6.3-6.8
|
1.5-2.0
|
2.5-3.0
|
|
1.0-2.0
|
|
|
<1.0
|
|
HTQ-6B
|
40-45
|
6.5-7.0
|
1.7-2.2
|
2.5-3.0
|
|
|
|
|
<1.0
|
|
HTQ-7
|
40-45
|
6.8-7.3
|
1.5-2.0
|
2.5-3.0
|
|
|
|
|
<1.0
|
|
HTQ8-3
|
40-45
|
7.5-8.5
|
2.5-3.5
|
2.5-3.0
|
|
|
|
|
<1.0
|
|
HTQ8-5
|
40-45
|
7.5-8.5
|
4.0-6.0
|
<3.0
|
|
|
|
|
<1.0
|
|
二、厚大斷面球化劑
|
|
|
|
|
|
|
|
|
<1.0
|
|
D-1
|
40-45
|
6.5-7.0
|
2.0-2.5(重稀土)
|
2.2-2.8
|
|
1.5-2.0
|
適量
|
|
<1.0
|
|
D-2
|
40-45
|
7.5-8.0
|
2.0-2.5(重稀土)
|
2.2-2.8
|
|
1.5-2.0
|
適量
|
|
<1.0
|
|
三、珠光體球化劑
|
|
|
|
|
|
|
|
|
|
|
Z-1
|
40-45
|
6.5-7.0
|
1.5-2.0
|
2.5-3.0
|
|
|
|
適量
|
<1.0
|
|
Z-1A
|
40-45
|
6.0-6.5
|
1.5-2.0
|
2.3-2.8
|
|
|
|
適量
|
<1.0
|
|
Z-2
|
40-45
|
7.5-8.0
|
2.5-3.0
|
2.5-3.0
|
|
|
|
適量
|
|
|
四、Ni-Mg系
|
|
16-20
|
|
|
80-84
|
|
|
|
<1.0
|
|
五、風電球化劑
|
|
|
|
|
|
|
|
|
<1.0
|
|
F-1
|
40-45
|
6.5-7.0
|
1.0-1.5(重稀土)
|
2.0-2.5
|
|
1.5-2.0
|
適量
|
適量
|
<1.0
|
包裝:25Kg編織袋和1000Kg噸裝袋，也可根據用戶要求包裝。
粒度:3-15mm,5-25mm,5-30mm,也可以根據用戶要求的粒度范圍加工供貸。
特點:球化能力強，無衰退之憂:成份穩(wěn)定，波動范圍小、偏析小、組織均勻：Mg0含量低，反應平穩(wěn)，Mg吸收率高，使用安全：球化劑添加量少，氧化物少，夾渣少
|